5083 grade aluminum is the representative product of 5000 series aluminum alloy, the state is mostly O, H32, H111, H321, H116, commonly used in ships and tanker body. 5083 grade aluminum alloy is a high magnesium alloy, the main alloying element is magnesium, with good forming and processing performance, corrosion resistance, weldability, medium strength, used in the manufacture of aircraft fuel tanks, fuel lines, and transportation vehicles, ships, sheet metal parts, instrumentation, street lamps brackets and rivets, hardware, electrical enclosures.
5083 grade aluminium alloy has good forming and processing performance, can be tensile, bending, flanging, spinning and other processing operations, and has good deep drawing performance. In addition, 5083 grade aluminum alloy welding performance is also good, can be fusion welding, pressure welding and brazing and other operations, suitable for manufacturing needs to be connected into a large area of the plate parts.
It should be noted that in the forming process, the 5083 aluminum alloy needs to be operated according to its characteristics because of its high strength, which requires the use of large forming force, and its good corrosion resistance. In addition, 5083 grade aluminum alloy may produce cracks during processing, which need to be treated and quality controlled accordingly.
5083 grade aluminium alloy is a medium strength aluminum alloy, its tensile strength is usually between 240-280 MPa, depending on the specific alloy state and heat treatment conditions. In addition, 5083 grade aluminum alloy also has good corrosion resistance and is suitable for use in marine environments, where it can effectively resist the erosion of corrosive media such as seawater, sea air and sea salt, extending the service life of the material. Therefore, 5083 grade aluminum alloy is widely used in shipbuilding and ocean engineering and other fields.